carbon steel pipe l stainless steel tube l hollow section

LSAW Steel Pipe (Longitudinally Submerged Arc Welding Pipe)

Straight Seam Submerged Arc Welded Steel Pipe

UOE SAWL PIPES

Outside Diameter：Φ508mm- 1118mm (20"- 44")

Wall Thickness: 6.0-25.4mm 1/4"-1"
Quality Standards: API、DNV、ISO、DEP、EN、ASTM、DIN、BS、JIS、GB、CSA
Length: 9-12.3m (30'- 40')
Grades: API 5L A-X90,GB/T9711 L190-L625

JCOE SAWL PIPES

Outside Diameter：Φ406mm- 1626mm (16" - 64" )
Wall Thickness：6.0- 75mm (1/4" - 3" )
Quality Standards：API、DNV、ISO、DEP、EN、ASTM、DIN、BS、JIS、GB、CSA
Length：3-12.5m ( 10'- 41' )
Grades：API 5L A-X100, GB/T9711 L190-L690

Tolerance of Outside Diameter and Wall Thickness

Types	Standard
Types	SY/T5040-2000	SY/T5037-2000	SY/T9711.1-1977	ASTM A252	AWWA C200-97	API 5L PSL1
Tube end OD deviation	±0.5%D	±0.5%D	-0.79mm～+2.38mm	<±0.1%T	<±0.1%T	±1.6mm
Wall thickness	±10.0%T	D<508mm, ±12.5%T	-8%T～+19.5%T	<-12.5%T	-8%T～+19.5%T	5.0mm
Wall thickness	±10.0%T	D>508mm, ±10.0%T	-8%T～+19.5%T	<-12.5%T	-8%T～+19.5%T	T≥15.0mm, ±1.5mm

Chemical Composition and Mechanical Properties of LSAW Steel Pipe

Standard	Grade	Chemical Composition(max)%					Mechanical Properties(min)
Standard	Grade	C	Mn	Si	S	P	Yield Strength (Mpa)	Tensile Strength (Mpa)
GB/T700-2006	A	0.22	1.4	0.35	0.050	0.045	235	370
	B	0.2	1.4	0.35	0.045	0.045	235	370
	C	0.17	1.4	0.35	0.040	0.040	235	370
	D	0.17	1.4	0.35	0.035	0.035	235	370
GB/T1591-2009	A	0.2	1.7	0.5	0.035	0.035	345	470
	B	0.2	1.7	0.5	0.030	0.030	345	470
	C	0.2	1.7	0.5	0.030	0.030	345	470
BS En10025	S235JR	0.17	1.4	-	0.035	0.035	235	360
	S275JR	0.21	1.5	-	0.035	0.035	275	410
	S355JR	0.24	1.6	-	0.035	0.035	355	470
DIN 17100	ST37-2	0.2	-	-	0.050	0.050	225	340
	ST44-2	0.21	-	-	0.050	0.050	265	410
	ST52-3	0.2	1.6	0.55	0.040	0.040	345	490
JIS G3101	SS400	-	-	-	0.050	0.050	235	400
JIS G3101	SS490	-	-	-	0.050	0.050	275	490
API 5L PSL1	A	0.22	0.9	-	0.03	0.03	210	335
	B	0.26	1.2	-	0.03	0.03	245	415
	X42	0.26	1.3	-	0.03	0.03	290	415
	X46	0.26	1.4	-	0.03	0.03	320	435
	X52	0.26	1.4	-	0.03	0.03	360	460
	X56	0.26	1.1	-	0.03	0.03	390	490
	X60	0.26	1.4	-	0.03	0.03	415	520
	X65	0.26	1.45	-	0.03	0.03	450	535
	X70	0.26	1.65	-	0.03	0.03	585	570

Production equipment of lsaw steel pipe

Plate edge milling machine
The milling machine mills the two sides of the plate to exacting standards in order to meet width, edging and groove shape specifications.

Edge crimping machine
The crimping machine crimps the edges of the plate to form the required curvature.

Tack welding machine
The two edges of the open seam pipe are brought together by the tack welding machine. then welded by the tack welder using a metal active - gas arc welding("MAG" )process.

Forming machine
Utilizes the "JCO" process to bend and form the crimped steel plate into a steel pipe.

Interior welding machine
The interior longitudinal seam of the pipe is welded from the inside by fixing 4 welding heads while moving pipe and using submerged-arc welding process.

End facing machine
The machine levels the pipe end with rotating cutter heads to ensure that required groove and edge specifications are met.

Hydrostatic tester
Using end face sealing technology eliminates blind zones during hydrostatic testing. The tester is also equipped with automatic recording and storing functions.

Expanding machine
The pipe is subjected to full-length expansion to increase the precision of the pipe dimensions and to improve the internal stress distribution.

Automated ultrasonic testing equipment
The superiority of phased arrayultra sonic technology:
(1 )Adopting electron control method for fast linear scanning or sector scanning without moving probe or moving less. thus greatlyim prove detection efficiency.
(2)Controlting the sound beam by setting detection angles, its good sound beam reachability can enhances reliability and accuracy of detection.
(3) Dynamic control the deflection and focus of sound beam realizes the detection of pipes with different wall thickness without replacing probes.